Semi-Permanent for Rubber Mold Release Coating-科慕杜邦特氟龙涂料铁氟龙TeflonStonerTraSys818水性脱模剂Oring喷涂轮胎模具特氟龙TuframPPA571专业网站

Semi-Permanent for Rubber Mold Release Coating

Molders specify ready-to-use Stoner™ TraSys® semi-permanent water-based rubber release coatings because they:

	TraSys® 9825	TraSys® 428	TraSys® 818	TraSys® 708
Release Type	Semi-Permanent	Semi-Permanent	Semi-Permanent	Semi-Permanent
Resin Carrier	Water	Water	Water	Water
Typical Uses	Injection, Transfer, General-Purpose	Compression Transfer, Injection, Higher Temp. Molding	Compression Transfer, Injection, General-Purpose, Touch-Up	Injection, Transfer, General-Purpose, Compression
Compatible Compounds	Fluoroelastomers, NBR, EPDM, Most Compounds	Organic Polymers	Organic Polymers and Natural Rubber	Fluoroelastomers, NBR, EPDM, Most Compounds
Apply to Mold	Hot Molding Temperature	Hot Molding Temperature	Hot Molding Temperature	Hot Molding Temperature
Min. Cure Temp. / Min. Cure Time	132°C (270°F) / 5 minutes	132°C (270°F) / 3 minutes	132°C (270°F) / 3 minutes	132°C (270°F) / 5 minutes
Maximum Operating Temperature	190°C (380°F)	232°C (450°F)	327°C (620°F)	205°C (401°F)
Agitation Required	Slight	Slight	Yes	Slight
Product Cosmetics	Satin	Semigloss	Satin	Satin
Affected by Freeze?	No	No	No	No
Comments	First Choice for Specialty Rubbers, Vamac®, Viton®, Aflas®. Excellent Ability to Bond to Plated or Polished Surfaces	Highest Slip. Good for High-Flow Injection Molding	Good for Rubber to Metal Bonding. Best for Silicone Elastomers. Good Touch-Up for Permanent Fluorochemicals	First Choice for Specialty Rubbers, Vamac®, Viton®, Aflas®. Excellent Ability to Bond to Plated or Polished Surfaces.

Non-ozone depleting, noncarcinogenic solvent, No VOC content.
Hot to the touch; approximately 48°-60°C (120°-140°F).
Inner mold temperature; normally accomplished by cycling coated mold when empty.
Air cures rapidly on substrates at 32°-38°C (70°-100°F). Introduction of 149°C (300°F) heat after application enhances cure and prolongs durability of coating.