 DuPont TraSys 420 Mold Release Coating

Description

DuPontTM TraSys® 420 mold release coating is a translucent water-based dispersion for rotational molding applications. When applied to a mold, it exhibits outstanding release or antistick properties and has a very low coefficient of friction. It is clean, nonoily, nonstaining, chemically inert, and can function in temperatures to 260°C (500°F) or higher.

TraSys® 420 will meet molders’ production, environmental, and safety requirements. It offers an unmatched combination of lubricity and durability, without the use of silicone oils, providing consistent release and reducing mold buildup. TraSys® 420 is solvent-free, meeting all existing and anticipated environmental regulations. Additionally, TraSys® 420 contains no alcohols that may form flammable vapors. 

Uses

TraSys® 420 is ideal for rotational mold internals and other molding applications where a consistent, controlled release is desired.

Directions for Use

TraSys® 420 must be agitated before use. TraSys® 420
mold release coating should be applied to clean and dry surfaces. For maximum results, preheat the mold surface to 55–60°C (130–140°F) before application. 

Recommended Procedure 

Clean mold thoroughly, using glass or plastic bead media, abrasive pads, and cleaning solvent or high pH detergent, to remove all prior mold release and other sources of contamination.

If spraying, use spray equipment that provides a fine mist. When wiping, lightly dampen a clean cloth with TraSys® 420 after agitation. After agitation, apply lightly to the mold’s surfaces, making certain that all areas of the mold are entirely coated.

A minimum inner mold temperature of 132°C (270°F)
is recommended to cure the release. This can easily be accomplished after application by running the mold empty through a full production cycle with the oven temperature at 170°C (350°F). Proper curing will give a bond between mold and coating that will ensure no transfer of coating to the first molded part, as well as ensure the most effective coating for durability and cycle life.

When spot touch-ups are applied, curing the freshly coated area with a heat gun will further enhance the bond between the coating and the mold’s surface. Larger applications may require a bake cycle as described above.

Typical Properties

Primary Polymer: Specific Gravity: Odor:
Color:

Flash Point:

Thermoset Polysiloxanes 1.0
Slight
White

None 

 

Storage and Handling

DuPontTM TraSys® 420 should be stored in a cool, dry, well ventilated area. Do not expose to freezing temperatures. Freezing will affect the physical condition, but will not damage the release effectiveness. Thaw at room temperature, and mix well before using.

Containers in use should be agitated before use and often during use. Drums will require a low rpm agitator to prevent phase separation in the storage container.

Breathing vapors should be avoided. If spraying, care should be taken to avoid inhaling mist or vapors, just as sprayed paint inhalation should be avoided.

Care should be taken not to expose TraSys® 420 mold release coating to open flame or intense heat. Temperatures above 260°C (500°F) may cause chemical breakdown, resulting in toxic fumes. Always wash hands after handling TraSys® 420 mold release coating.

Shelf Life

TraSys® 420 has a shelf life of 1 year from the date of manufacture. The date of manufacture and shelf life are posted on the container label.

Packaging

TraSys® 420 is available in 1-, 5-, and 55-gal containers. Larger volume orders may be packaged in specialty containers.

Shipping Limitations

None 

产品关键词:Teflon涂料|杜邦特氟龙涂料|XYLAN涂料|TUFRAM|STONER脱模剂|TRASYS水性脱模剂|滚塑脱模剂|硅胶脱模剂|聚氨酯PU脱模剂|热塑性塑料脱模剂|碳纤维脱模剂|胶管脱模剂|复合材料脱模剂|半钢轮胎涂料|球模铁氟龙涂料|鞋模铁氟龙涂料|园林剪刀铁氟龙涂料|吸塑模铁氟龙涂料|医疗器械涂层|橡胶表面特氟龙喷涂|O型圈PTFE喷涂|耐磨自润滑涂料|二硫化钼涂料|轴瓦涂料|真空泵无油转子涂料|灯泡防爆PFA粉末TraSys818|TraSys420|TraSys9825|TraSys428|TraSys423|电子清洗剂\3M PFA静电喷涂级粉末|Whitford PFA喷涂粉末

Chemours/Teflon/科慕/特氟龙/铁氟龙商标品牌为美国科慕公司The Chemours Company所拥有